A study of PbS nanoparticle synthesis via sulfur powder

Department of Physics, St. John’s University, Jamaica, NY 11439, USA

Topical Section: Nanomaterials, nanoscience and nanotechnology

PbS nanoparticles (NPs) were synthesized by the hot-injection solution-phase method using sulfur powder as precursor. Pb-precursor (446 mg PbO) was dissolved with 1.5 ml oleic acid in 15 ml 1-octadecene (ODE) solvent inside a four-neck flask under N2 atmosphere and nucleated at 120 °C for half an hour. S-precursor (S powder), dissolved in a mixture of 3 ml ODE and 1 ml Oleylamine, was then injected swiftly by a syringe into the flask with well-dissolved Pb-precursor. The growth time varied from 10 minutes to a few hours and growth temperature was maintained at from 90 to 120 °C after injection, which would result in nanoparticles of different sizes from 5 to 10 nm. The synthesized PbS NPs were characterized by TEM, XRD, and UV-Vis-NIR spectrometer. The morphology as well as absorption spectra were found to be highly sensitive to the synthesis conditions. The XRD spectra showed that the structures were less sensitive to synthesis conditions.
  Figure/Table
  Supplementary
  Article Metrics

Keywords synthesis; nanoparticles; hot-injection; characterization; lead sulfide; sulfur powder

Citation: Gen Long, Kenneth Sabalo, Raheeb Alsaidi, Michael Beattie, Blawal Chaudhry, Mohammad Khan, Juhayer Uddin, Mostafa Sadoqi. A study of PbS nanoparticle synthesis via sulfur powder. AIMS Materials Science, 2017, 4(2): 515-521. doi: 10.3934/matersci.2017.2.515

References

  • 1. Murray C, Norris D, Bawendi M (1993) Synthesis and characterization of nearly monodisperse CdE (E = S, Se, Te) semiconductor nanocrystallites. J Am Chem Soc 115: 8706–8715.    
  • 2. Machol J, Wise F, Patelb R, et al. (1994) Optical studies of IV–VI quantum dots. Physica A 207: 427–434.    
  • 3. Wise F (2000) Lead Salt Quantum Dots:  the Limit of Strong Quantum Confinement. Accounts Chem Res 33: 773–780.    
  • 4. Kramer I, Sargent E (2014) The Architecture of Colloidal Quantum Dot Solar Cells: Materials to Devices. Chem Rev 114: 863–882.
  • 5. Talapin D, Murray C (2005) PbSe nanocrystal solids for n- and p-channel thin film field-effect transistors. Science 310: 86–89.    
  • 6. McDonald S, Konstantatos G, Zhang S, et al. (2005) Solution-processed PbS quantum dot infrared photodetectors and photovoltaics. Nat Mater 4: 138–142.    
  • 7. Hines M, Scholes G (2003) Colloidal PbS Nanocrystals with Size-Tunable Near-Infrared Emission: Observation of Post-Synthesis Self-Narrowing of the Particle Size Distribution. Adv Mater 15: 1844–1849.    
  • 8. Warner J, Thomsen E, Watt A, et al. (2004) Time-resolved photoluminescence spectroscopy of ligand-capped PbS nanocrystals. Nanotechnology 16: 175–179.
  • 9. Cademartiri L, Montanari E, Calestani G, et al. (2006) Size-Dependent Extinction Coefficients of PbS Quantum Dots. J Am Chem Soc 128: 10337–10346.    
  • 10. Zhang D, Song J, Zhang J, et al. (2013) A facile and rapid synthesis of lead sulfide colloidal quantum dots using in situ generated H2S as the sulfur source. CrystEngComm 15: 2532–2536.    
  • 11. Kim E, Chung W, Lim J, et al. (2014) One-pot synthesis of PbS NP/sulfur-oleylamine copolymer nanocomposites via the copolymerization of elemental sulfur with oleylamine. Polym Chem 5: 3617–3623.    
  • 12. Liu J, Yu H, Wu Z, et al. (2009) Size-tunable near-infrared PbS nanoparticles synthesized from lead carboxylate and sulfur with oleylamine as stabilizer. Nanotechnology 19: 345602.
  • 13. Long G, Barman B, Delikanli S, et al. (2012) Carrier-dopant exchange interactions in Mn-doped PbS colloidal quantum dots. Appl Phys Lett 101: 062410.    

 

Reader Comments

your name: *   your email: *  

Copyright Info: 2017, Gen Long, et al., licensee AIMS Press. This is an open access article distributed under the terms of the Creative Commons Attribution Licese (http://creativecommons.org/licenses/by/4.0)

Download full text in PDF

Export Citation

Copyright © AIMS Press All Rights Reserved