Synthesis of easily sinterable ceramic electrolytes based on Bi-doped 8YSZ for IT-SOFC applications

  • Received: 20 March 2019 Accepted: 29 May 2019 Published: 08 July 2019
  • Ceramic electrolytes formed by Bi (4 mol%)-doped 8YSZ, i.e., Y2O3 (8 mol%)-doped ZrO2, were synthesized by a simple co-precipitation route, using ammonia solution as precipitating agent. The amorphous as-synthesized powders convert into zirconia-based single phase with fluorite structure through a mild calcination step at 500 °C. The calcined powders were sintered at very low temperatures (i.e., 900–1100 °C) achieving in both cases very high values of relative densities (i.e., >95%); the corresponding microstructures were highly homogeneous and characterized by micrometric grains or sub-micrometric grains for sintering at 1100 °C and 900 °C, respectively. Very interesting electrochemical properties were determined by Electrochemical Impedance Spectroscopy (EIS) in the best samples. In particular, their total ionic conductivity, recorded at 650 °C, are 6.06 × 10-2S/cm and 4.44 × 10-2S/cm for Bi (4 mol%)-doped 8YSZ sintered at 1100 °C and 900 °C, respectively. Therefore, Bi was proved to be an excellent sintering aid dopant for YSZ, highly improving its densification at lower temperatures while increasing its total ionic conductivity.

    Citation: Luca Spiridigliozzi, Grazia Accardo, Emilio Audasso, Barbara Bosio, Sung Pil Yoon, Gianfranco Dell’Agli. Synthesis of easily sinterable ceramic electrolytes based on Bi-doped 8YSZ for IT-SOFC applications[J]. AIMS Materials Science, 2019, 6(4): 610-620. doi: 10.3934/matersci.2019.4.610

    Related Papers:

  • Ceramic electrolytes formed by Bi (4 mol%)-doped 8YSZ, i.e., Y2O3 (8 mol%)-doped ZrO2, were synthesized by a simple co-precipitation route, using ammonia solution as precipitating agent. The amorphous as-synthesized powders convert into zirconia-based single phase with fluorite structure through a mild calcination step at 500 °C. The calcined powders were sintered at very low temperatures (i.e., 900–1100 °C) achieving in both cases very high values of relative densities (i.e., >95%); the corresponding microstructures were highly homogeneous and characterized by micrometric grains or sub-micrometric grains for sintering at 1100 °C and 900 °C, respectively. Very interesting electrochemical properties were determined by Electrochemical Impedance Spectroscopy (EIS) in the best samples. In particular, their total ionic conductivity, recorded at 650 °C, are 6.06 × 10-2S/cm and 4.44 × 10-2S/cm for Bi (4 mol%)-doped 8YSZ sintered at 1100 °C and 900 °C, respectively. Therefore, Bi was proved to be an excellent sintering aid dopant for YSZ, highly improving its densification at lower temperatures while increasing its total ionic conductivity.


    加载中


    [1] Panthi D, Tsutsumi A (2014) Micro-tubular solid oxide fuel cell based on a porous yttria-stabilized zirconia support. Sci Rep 4: 5754.
    [2] Nagao M, Kobayashi K, Hibino T (2014) Low-temperature sintering of yttria-stabilized zirconia using bismuth-vanadium oxide as a sintering aid at 800 °C. Chem Lett 43: 1887–1889. doi: 10.1246/cl.140712
    [3] Dell'Agli G, Mascolo G (2003) Sinterability of 8Y-ZrO2 powders hydrothermally synthesized at low temperature. Solid State Ionics 160: 363–371. doi: 10.1016/S0167-2738(03)00205-4
    [4] Barad C, Shekel G, Shandalov M, et al. (2017) Internal nano voids in yttria stabilized zirconia (YSZ) powder. Materials 10: 1440. doi: 10.3390/ma10121440
    [5] Shekel G, Barad C, Hayun H, et al. (2018) Applying the general effective media (GEM) approach for analyzing the thermal conductivity of ZrO2-8YSZ composites. Phys Chem Chem Phys 20: 16666–16672. doi: 10.1039/C8CP00824H
    [6] Barad C, Shamir D, Cahana M, et al. (2019) Influence of galia (Ga2O3) addition on the phase evolution and grain growth behavior of voided yttria stabilized zirconia (YSZ) powder. J Alloy Compd 783: 286–291. doi: 10.1016/j.jallcom.2018.12.318
    [7] Joh DW, Park JH, Kim D, et al. (2017) Functionally graded bismuth oxide/zirconia bilayer electrolytes for high performance intermediate-temperature solid oxide fuel cells (IT-SOFCs) ACS Appl Mater Inter 9: 8443–8449.
    [8] Spiridigliozzi L, Dell'Agli G, Biesuz M, et al. (2016) Effect of the precipitating agent on the synthesis and sintering behavior of 20 mol Sm-doped ceria. Adv Mater Sci Eng 2016: 6096123.
    [9] Dell'Agli G, Spiridigliozzi L, Pansini M, et al. (2018) Effect of the carbonate environment on morphology and sintering behaviour of variously co-doped (Ca, Sr, Er, Pr) Samarium-doped Ceria in co-precipitation/hydrothermal synthesis. Ceram Int 44: 17935–17944. doi: 10.1016/j.ceramint.2018.06.269
    [10] Jaiswala N, Tanwar K, Suman R, et al. (2019) A brief review on ceria based solid electrolytes for solid oxide fuel cells. J Alloy Compd 781: 984–1005. doi: 10.1016/j.jallcom.2018.12.015
    [11] Jolley AG, Jayathilake R, Wachsman ED (2019) Optimizing rhombohedral Bi2O3 conductivity for low temperature SOFC electrolytes. Ionics 2019: 1–6.
    [12] Flegler AJ, Burye TE, Yang Q, et al. (2014) Cubic yttria stabilized zirconia sintering additive impacts: a comparative study. Ceram Int 40: 16323–16335. doi: 10.1016/j.ceramint.2014.07.071
    [13] Mahato N, Banerjee A, Gupta A, et al. (2015) Progress in material selection for solid oxide fuel cell technology: a review. Prog Mater Sci 72: 141–337. doi: 10.1016/j.pmatsci.2015.01.001
    [14] Da SFS, De STM (2017) Novel materials for solid oxide fuel cell technologies: a literature review. Int J Hydrogen Energ 42: 26020–26036. doi: 10.1016/j.ijhydene.2017.08.105
    [15] Accardo G, Frattini D, Ham HC, et al. (2018) Improved microstructure and sintering temperature of bismuth nano-doped GDC powders synthesized by direct sol-gel combustion. Ceram Int 44: 3800–3809. doi: 10.1016/j.ceramint.2017.11.165
    [16] Liu L, Zhou Z, Tian H, et al. (2016) Effect of bismuth oxide on the microstructure and electrical conductivity of yttria stabilized zirconia. Sensors 16: 369–379. doi: 10.3390/s16030369
    [17] Dell'Agli G, Mascolo G, Mascolo MC, et al. (2005) Crystallization-stabilization mechanism of yttria-doped zirconia by hydrothermal treatment of mechanical mixtures of zirconia xerogel and crystalline yttria. J Cryst Growth 280: 255–265. doi: 10.1016/j.jcrysgro.2005.03.004
    [18] Akhtar K, Haq IU, Hira U (2013) Synthesis and characterization of uniform zirconia particles by homogeneous precipitation method. High Temp Mat Pr 32: 391–395.
    [19] Accardo G, Dell'Agli G, Frattini D, et al. (2017) Electrical behaviour and microstructural characterization of magnesia co-doped ScSZ nanopowders synthesized by urea co-precipitation. Chem Eng T 57: 1345–1350.
    [20] Da Silva CA, Ribeiro NFP, Souza MMVM (2009) Effect of the fuel type on the synthesis of yttria stabilized zirconia by combustion method. Ceram Int 35: 3441–3446. doi: 10.1016/j.ceramint.2009.06.005
    [21] Ghahfarokhi SS, Mamoory RS, Kalashami AG (2018) Inverse precipitation synthesis of ZrO2 nanopowder and in-situ coating on MWCNTs. Ceram Int 44: 13556–13564. doi: 10.1016/j.ceramint.2018.04.188
    [22] Barad C, Kimmel G, Hayun H, et al. (2018) Influence of galia (Ga2O3) addition on phase transitions and crystal growth of zirconia (ZrO2). J Mater Sci 53: 12741–12749. doi: 10.1007/s10853-018-2556-1
    [23] Razik NA (1985) Precise lattice constants determination of cubic crystals from x-ray powder diffractometric measurements. Appl Phys A-Mater 37: 187–189. doi: 10.1007/BF00617505
    [24] Dell'Agli G, Mascolo G, Mascolo MC, et al. (2008) Drying effect on thermal behaviour and structural modification of hydrous zirconia gel. J Am Ceram Soc 91: 3375–3379. doi: 10.1111/j.1551-2916.2008.02635.x
    [25] Dell'Agli G, Mascolo G, Mascolo MC, et al. (2006) Weakly-agglomerated nanocrystalline (ZrO2)0.9(Yb2O3)0.1 powders hydrothermally synthesized at low temperature. Solid State Sci 8: 1046–1050.
    [26] Kim DJ (1989) Lattice parameters, ionic conductivities, and solubility limits in fluorite-structure MO2 oxide (M = Hf4+, Zr4+, Ce4+, Th4+, U4+) solid solutions. J Am Ceram Soc 72: 1415–1421. doi: 10.1111/j.1151-2916.1989.tb07663.x
    [27] Andini S, Montagnaro F, Santoro L, et al. (2018) Mechanochemical processing of blast furnace slag for its reuse as adsorbent. Chem Eng T 32: 22 99–2304.
    [28] Frattini D, Accardo G, Moreno A, et al. (2017) A novel nickel-aluminum alloy with titanium for improved anode performance and properties in molten carbonate fuel cells. J Power Sources 352: 90–98. doi: 10.1016/j.jpowsour.2017.03.112
    [29] Spiridigliozzi L, Dell'Agli G, Marocco A, et al. (2018) Engineered co-precipitation chemistry with ammonium carbonate for scalable synthesis and sintering of improved Sm0.2Ce0.8>O1.90 and Gd0.16Pr0.04Ce0.8O1.90 electrolytes for IT-SOFCs. J Ind Eng Chem 59: 17–27.
  • Reader Comments
  • © 2019 the Author(s), licensee AIMS Press. This is an open access article distributed under the terms of the Creative Commons Attribution License (http://creativecommons.org/licenses/by/4.0)
通讯作者: 陈斌, bchen63@163.com
  • 1. 

    沈阳化工大学材料科学与工程学院 沈阳 110142

  1. 本站搜索
  2. 百度学术搜索
  3. 万方数据库搜索
  4. CNKI搜索

Metrics

Article views(3921) PDF downloads(990) Cited by(4)

Article outline

Figures and Tables

Figures(8)

/

DownLoad:  Full-Size Img  PowerPoint
Return
Return

Catalog