Evolution of activation energy during hot deformation of Al–15% B4C composites containing Sc and Zr

1 Department of Applied Science, University of Quebec at Chicoutimi, Saguenay (QC), Canada G7H 2B1
2 High-performance metal structural materials research institute, Soochow University, Suzhou, 215021, China

Topical Section: Materials Processing

During hot deformation, the activation energy, Q, is an essential parameter that indicates the difficulty level in the hot working processing. The evolution of the activation energies of three Al–15% B4C composites (the base material, S40 with 0.4% Sc and SZ40 with 0.4% Sc and 0.2% Zr) was investigated using high-temperature flow stress data based on a revised Sellar’s constitutive equation. The microstructure evolution during hot deformation was characterized using a transmission electron microscope. The calculated activation energy maps reveal that the activation energy during hot deformation was related to the microstructure change in addition to deformation conditions. For the base composite, the variation of the activation energy was small because the microstructure barely changed during deformation. For the Sc and Zr containing composites (S40 and SZ40), dynamic precipitation occurred at high deformation temperature and the activation energy map can be divided in two regions. The activation energy decreases with an increase of deformation temperature to the minimum level in the region I where the composites were in the solid solution condition. It follows by an increase with increasing temperature in the region II where dynamic precipitation occurred. Based on the combination of the activation energy map with the flow instability zone, the optimum hot workability of a composite in term of excellent processability was proposed at the domain where the less energy of hot deformation was required.
  Figure/Table
  Supplementary
  Article Metrics

Keywords Al–B4C composites; activation energy map; high-temperature flow stress; Sc and Zr addition; dynamic precipitation

Citation: Jian Qin, Zhan Zhang, X.-Grant Chen. Evolution of activation energy during hot deformation of Al–15% B4C composites containing Sc and Zr. AIMS Materials Science, 2019, 6(4): 484-497. doi: 10.3934/matersci.2019.4.484

References

  • 1. Bonnet G, Rohr V, Chen XG, et al. (2009) Use of Alcan's Al–B4C metal matrix composites as neutron absorber material in TN International's transportation and storage casks. Packag Transp Storage Secur Radioact Mater 20: 98–102.    
  • 2. Fuller CB, Seidman DN, Dunand DC (2003) Mechanical properties of Al(Sc,Zr) alloys at ambient and elevated temperatures. Acta Mater 51: 4803–4814.    
  • 3. Lai J, Zhang Z, Chen XG (2012) The thermal stability of mechanical properties of Al–B4C composites alloyed with Sc and Zr at elevated temperatures. Mat Sci Eng A-Struct 532: 462–470.    
  • 4. Lai J, Zhang Z, Chen XG (2013) Precipitation strengthening of Al–B4C metal matrix composites alloyed with Sc and Zr. J Alloy Compd 552: 227–235.    
  • 5. Qin J, Zhang Z, Chen XG (2014) Effect of hot deformation on microstructure and mechanical properties of Al–B4C composite containing Sc. Mater Sci Forum 794–796: 821–826.
  • 6. Qin J, Zhang Z, Chen XG (2016) Mechanical Properties and Strengthening Mechanisms of Al-15 Pct B4C Composites with Sc and Zr at Elevated Temperatures. Metall Mater Trans A 47: 4694–4708.    
  • 7. Qin J, Zhang Z, Chen XG (2017) Hot Deformation and Processing Maps of Al–15%B4C Composites Containing Sc and Zr. J Mater Eng Perform 26: 1673–1684.    
  • 8. Qin J, Zhang Z, Chen XG (2017) Mechanical properties and thermal stability of hot-rolled Al–15%B4C composite sheets containing Sc and Zr at elevated temperature. J Compos Mater 51: 2643–2653.    
  • 9. Sellars C, Tegart WMG (1966) Relation between flow stress and structure in hot deformation. Mem Etud Sci Rev Met 67: 731–746.
  • 10. Shi C, Chen XG (2014) Effect of Zr addition on hot deformation behavior and microstructural evolution of AA7150 aluminum alloy. Mat Sci Eng A-Struct 596: 183–193.    
  • 11. Jin N, Zhang H, Han Y, et al. (2009) Hot deformation behavior of 7150 aluminum alloy during compression at elevated temperature. Mater Charact 60: 530–536.    
  • 12. Li Y, Liu Z, Lin L, et al. (2011) Deformation behavior of an Al–Cu–Mg–Mn–Zr alloy during hot compression. J Mater Sci 46: 3708–3715.    
  • 13. McQueen HJ, Spigarelli S, Kassner ME, et al. (2011) Hot deformation and processing of aluminum alloys, Boca Raton: CRC Press.
  • 14. Shi CJ, Mao WM, Chen XG (2013) Evolution of activation energy during hot deformation of AA7150 aluminum alloy. Mat Sci Eng A-Struct 571: 83–91.    
  • 15. Shi C, Chen XG (2016) Evolution of activation energies for hot deformation of 7150 aluminum alloys with various Zr and V additions. Mat Sci Eng A-Struct 650: 197–209.    
  • 16. Wang S, Hou LG, Luo JR, et al. (2015) Characterization of hot workability in AA 7050 aluminum alloy using activation energy and 3-D processing map. J Mater Process Tech 225: 110–121.    
  • 17. Peng X, Su W, Xiao D, et al. (2018) Investigation on Hot Workability of Homogenized Al-Zn-Mg-Cu Alloy Based on Activation Energy and Processing Map. JOM 70: 993–999.    
  • 18. Malas JC, Venugopal S, Seshacharyulu T (2004) Effect of microstructural complexity on the hot deformation behavior of aluminum alloy 2024. Mat Sci Eng A-Struct 368: 41–47.    
  • 19. El-Danaf EA, AlMajid AA, Soliman MS (2008) Hot deformation of AA6082-T4 aluminum alloy. J Mater Sci 43: 6324.    
  • 20. Huang X, Zhang H, Han Y, et al. (2010) Hot deformation behavior of 2026 aluminum alloy during compression at elevated temperature. Mat Sci Eng A-Struct 527: 485–490.    
  • 21. Zhang H, Li L, Yuan D, et al. (2007) Hot deformation behavior of the new Al–Mg–Si–Cu aluminum alloy during compression at elevated temperatures. Mater Charact 58: 168–173.    
  • 22. Cerri E, Evangelista E, Forcellese A, et al. (1995) Comparative hot workability of 7012 and 7075 alloys after different pretreatments. Mat Sci Eng A-Struct 197: 181–198.    
  • 23. Johnson GR, Cook WH (1985) Fracture characteristics of three metals subjected to various strains, strain rates, temperatures and pressures. Eng Fract Mech 21: 31–48.    
  • 24. Samantaray D, Mandal S, Bhaduri AK (2010) Constitutive analysis to predict high-temperature flow stress in modified 9Cr–1Mo (P91) steel. Mater Design 31: 981–984.    
  • 25. McQueen HJ, Blum W (2000) Dynamic recovery: sufficient mechanism in the hot deformation of Al (<99.99). Mat Sci Eng A-Struct 290: 95–107.    
  • 26. Wouters P, Verlinden B, McQueen HJ, et al. (1990) Effect of homogenization and precipitation treatments on the hot workability of an aluminium alloy AA2024. Mat Sci Eng A-Struct 123: 239–245.    
  • 27. Prasad Y, Sasidhara S (1997) Hot working guide: a compendium of processing maps, ASM international.
  • 28. Prasad Y (2003) Processing maps: a status report. J Mater Eng Perform 12: 638–645.    

 

Reader Comments

your name: *   your email: *  

© 2019 the Author(s), licensee AIMS Press. This is an open access article distributed under the terms of the Creative Commons Attribution Licese (http://creativecommons.org/licenses/by/4.0)

Download full text in PDF

Export Citation

Copyright © AIMS Press All Rights Reserved