Lead, zinc and copper fine powder with controlled size and shape

  • Received: 01 August 2017 Accepted: 07 November 2017 Published: 14 December 2017
  • This study describes the preparation of lead, zinc and copper powders by hydrometallurgy from secondary resources. Chloride, sulphate and acetate salts of zinc, copper and lead were prepared. The powders were prepared by reducing the ionic species of these metals by hydrazine hydrate or ascorbic acid. The effect of addition of some water soluble polar organic solvents to the aqueous salt solutions on the morphology and particle size of the prepared powder was studied. Findings were explained on the basis of the transition state theory and according to the Hughes and Ingold’s rule. Aqueous solutions alone produce metal powder having different size and irregular shape. The presence of polar organic solvents with high molecular weight and polarity produce powders having controlled size and regular morphology. The reason was because solvent polarity enhances the rate of red-ox reactions between metal ions and the reducing agent. The mean particle size of the powder was 60 um with zinc, 80 um with copper, and 90 um with lead. The extent of productivity was ≥98%. Results highlighted that the chemical reduction of the ionic species took place in a sequence steps. The first is a diffusion of the reactants across a boundary layer established at the polar site of the organic solvent molecules. The next step is the direct contact of the reactants. The third step involved reduction to yield powder. The last is the backward diffusion of the powder outside the boundary layer. Results showed that addition of water-miscible solvents having high dielectric constant increased the polarity of the medium. This energizes and enhances the one or more t step of the model to be more rapid to yield particles with small size and symmetrical shape.

    Citation: Mahmoud A Rabah. Lead, zinc and copper fine powder with controlled size and shape[J]. AIMS Materials Science, 2017, 4(6): 1358-1371. doi: 10.3934/matersci.2017.6.1358

    Related Papers:

  • This study describes the preparation of lead, zinc and copper powders by hydrometallurgy from secondary resources. Chloride, sulphate and acetate salts of zinc, copper and lead were prepared. The powders were prepared by reducing the ionic species of these metals by hydrazine hydrate or ascorbic acid. The effect of addition of some water soluble polar organic solvents to the aqueous salt solutions on the morphology and particle size of the prepared powder was studied. Findings were explained on the basis of the transition state theory and according to the Hughes and Ingold’s rule. Aqueous solutions alone produce metal powder having different size and irregular shape. The presence of polar organic solvents with high molecular weight and polarity produce powders having controlled size and regular morphology. The reason was because solvent polarity enhances the rate of red-ox reactions between metal ions and the reducing agent. The mean particle size of the powder was 60 um with zinc, 80 um with copper, and 90 um with lead. The extent of productivity was ≥98%. Results highlighted that the chemical reduction of the ionic species took place in a sequence steps. The first is a diffusion of the reactants across a boundary layer established at the polar site of the organic solvent molecules. The next step is the direct contact of the reactants. The third step involved reduction to yield powder. The last is the backward diffusion of the powder outside the boundary layer. Results showed that addition of water-miscible solvents having high dielectric constant increased the polarity of the medium. This energizes and enhances the one or more t step of the model to be more rapid to yield particles with small size and symmetrical shape.


    加载中
    [1] Thornton CP (2007) Of brass and bronze in prehistoric Southwest Asia. Papers and Lectures Online. Archetype Publications.
    [2] SahuandK K, Agrawal A (2017) Recycling of metals from secondary sources treatment options. Wikipedia, online 2017.
    [3] Solisio C, Marco P, Piergiorgio P, et al. (1999) Electrochemical remediationofcopper(II) from an industrial effluent. Part I: Monopolar plate electrodes. Resour Conserv Recy 26: 115–124.
    [4] Ahmed IM, Nayl AA, Daoud JA (2016) Leaching and recovery of zinc and copper from brass slag by sulfuric acid. J Saudi Chem Soc 20: S280–S285. doi: 10.1016/j.jscs.2012.11.003
    [5] Foda S, Rabah M (1999) Hydrometallurgical recovery of metal values from brass melting slag. Hydrometallurgy 53: 31–44. doi: 10.1016/S0304-386X(99)00030-4
    [6] Jha, MK, Kumar V, Singh RJ (2001) Review of hydrometallurgical recovery of zinc from industrial wastes. Resour Conserv Recy 33: 1–22. doi: 10.1016/S0921-3449(00)00095-1
    [7] Rabah MA, El-Sayed AS (1995) Recovery of zinc and some of its valuable salts from secondary resources and wastes. Hydrometallurgy 37: 23–32. doi: 10.1016/0304-386X(94)00015-U
    [8] Turan MD, Altundoğan, HS, Tümen F (2004) Recovery of zinc and lead from zinc plant residue. Hydrometallurgy 75: 169–176. doi: 10.1016/j.hydromet.2004.07.008
    [9] Hodjaoglu GA, Ivanov IS (2014) Metal recovery of solid metallurgical wastes. Galvanostatic electroextraction of copper from sulphate electrolytes containing Zn2+ and Fe2+ ions. Bulgarian Chem Commun 46: 150–156.
    [10] Meija J, Coplen TB, Berglund M, et al. (2016) Atomic weights of the elements 2013 (IUPAC Technical Report). Pure Appl Chem 88 : 265– 2 91.
    [11] Suganty K, Norita M (2003) Recovery of copper using an electro MP–Cell operated in anelectrogenerative mode. Sep Purif Technol 118: 279–284.
    [12] Weast R (1984) CRC, Handbook of Chemistry and Physics. Boca Raton, Florida: Chem Rubber Company Publishing. pp. E110.
    [13] Environmental Quality Act 1974 (Act 127), Regulations, Rules &Orders, International Law Book Services, Kuala Lumpur, 2009.
    [14] Skipton S, Hay D (1998) Drinking Water: Copper. Available from: http://www.ianr.unl.edu/pubs/Water/g1360.htm.
    [15] Chang FC, Lo SL, Ko CH (2007) Recovery of copper and chelating agents fromsludge extracting solutions. Sep Purif Technol 53: 49–56. doi: 10.1016/j.seppur.2006.06.011
    [16] Cay S, Uyanık A, Ozasik A (2004) Single and binary component adsorption ofcopper(II) and cadmium(II) from aqueous solutions using tea-industry waste. Sep Purif Technol 38: 273–280. doi: 10.1016/j.seppur.2003.12.003
    [17] Basha CA, Bhadrinarayana NS, Anantharaman N, et al. (2008) Heavymetal removal from copper smelting effluent using electrochemical cylindricalflow reactor. J Hazard Mater 152: 71–78. doi: 10.1016/j.jhazmat.2007.06.069
    [18] Chen JP, Lim LL (2002) Key factors in chemical reduction by hydrazine for recoveryof precious metals. Chemosphere 49: 363–370. doi: 10.1016/S0045-6535(02)00305-3
    [19] Jean-Pierre S, Paul B (2002) "Hydrazine" in Ullmann's Encyclopedia of Industrial Chemistry, Wiley-VCH, Weinheim, 2002.
    [20] Haws JL , Harden DG (1965) Thermodynamic Properties of Hydrazine . J Spacecraft Rockets 2 (6): 972–974 .
    [21] Eiblmaier J, Saller H, Heidelberg DG (2017) Outline PubChem, open chemistry database, online 4/45.
    [22] Wu S, Meng S (2005) Preparation of ultrafine silver powder using ascorbic acid as reducing agent and its application in MLCI. Mater Chem Phys 89: 423–427. doi: 10.1016/j.matchemphys.2004.09.026
    [23] .Fernandez-Merino MJ, Guardia L, Paredes JI, et al. (2010) Vitamin C Is an Ideal Substitute for Hydrazine in theReduction of Graphene Oxide Suspensions. J Phys Chem C 114: 6426–6432.
  • Reader Comments
  • © 2017 the Author(s), licensee AIMS Press. This is an open access article distributed under the terms of the Creative Commons Attribution License (http://creativecommons.org/licenses/by/4.0)
通讯作者: 陈斌, bchen63@163.com
  • 1. 

    沈阳化工大学材料科学与工程学院 沈阳 110142

  1. 本站搜索
  2. 百度学术搜索
  3. 万方数据库搜索
  4. CNKI搜索

Metrics

Article views(4890) PDF downloads(1349) Cited by(1)

Article outline

Figures and Tables

Figures(14)  /  Tables(2)

Other Articles By Authors

/

DownLoad:  Full-Size Img  PowerPoint
Return
Return

Catalog