Evaluation of tensile properties of ferrite single-phase low-carbon steel with different initial microstructures

  • Received: 11 June 2019 Accepted: 18 July 2019 Published: 02 September 2019
  • The tensile properties of ferrite single-phase low-carbon steel with different initial microstructures were evaluated. Three types of hot-rolled sheet specimens with different microstructures—specimen P (consisting of ferrite and pearlite), specimen B (consisting of bainitic structures), and specimen M (consisting of fully martensitic structures) were used. After hot rolling, these specimens were cold-rolled, subsequently heated to the finishing temperature of ferrite recrystallization, and then water-quenched to room temperature. The recrystallized ferrite grain size decreased in the specimen order of B > P > M. The distribution of cementite was comparatively homogeneous in specimens B and M, whereas that in specimen P was heterogeneous. The yield and tensile strengths decreased in the specimen order of M > P > B. Calculations using the Hall–Petch equation revealed that the yield strength of each specimen depended mainly on the recrystallized ferrite grain size. The total elongation decreased in the specimen order of B > P > M, whereas the local elongation was approximately the same in all of the specimens. In addition, the number of dimples decreased in the specimen order of M > B > P, whereas the size of dimples decreased in the specimen order of P > B > M. These results suggest that the homogeneous distribution of cementite and the fine recrystallized ferrite grains in specimen M suppress void coalescence, thereby resulting in a good balance between the tensile strength and the local elongation.

    Citation: Toshio Ogawa, Hiroyuki Dannoshita, Yoshitaka Adachi. Evaluation of tensile properties of ferrite single-phase low-carbon steel with different initial microstructures[J]. AIMS Materials Science, 2019, 6(5): 798-805. doi: 10.3934/matersci.2019.5.798

    Related Papers:

  • The tensile properties of ferrite single-phase low-carbon steel with different initial microstructures were evaluated. Three types of hot-rolled sheet specimens with different microstructures—specimen P (consisting of ferrite and pearlite), specimen B (consisting of bainitic structures), and specimen M (consisting of fully martensitic structures) were used. After hot rolling, these specimens were cold-rolled, subsequently heated to the finishing temperature of ferrite recrystallization, and then water-quenched to room temperature. The recrystallized ferrite grain size decreased in the specimen order of B > P > M. The distribution of cementite was comparatively homogeneous in specimens B and M, whereas that in specimen P was heterogeneous. The yield and tensile strengths decreased in the specimen order of M > P > B. Calculations using the Hall–Petch equation revealed that the yield strength of each specimen depended mainly on the recrystallized ferrite grain size. The total elongation decreased in the specimen order of B > P > M, whereas the local elongation was approximately the same in all of the specimens. In addition, the number of dimples decreased in the specimen order of M > B > P, whereas the size of dimples decreased in the specimen order of P > B > M. These results suggest that the homogeneous distribution of cementite and the fine recrystallized ferrite grains in specimen M suppress void coalescence, thereby resulting in a good balance between the tensile strength and the local elongation.


    加载中


    [1] Maki T, Onodera H, Tamura I (1975) Trip phenomenon in residual austenite of Fe–Ni–C alloy. J Soc Mater Sci 24: 150–155. doi: 10.2472/jsms.24.150
    [2] Matsumura O, Sakuma Y, Takechi H (1987) Enhancement of elongation by retained austenite in intercritical annealed 0.4C–1.5Si–0.8Mn steel. Trans ISIJ 27: 570–579.
    [3] Murata M, Kobayashi J, Sugimoto K (2010) Stretch-flangeability of ultra high-strength low alloy TRIP-aided sheet steels with mixed structure matrix of bainitic ferrite and martensite. Tetsu-to-Hagane 96: 84–92. doi: 10.2355/tetsutohagane.96.84
    [4] Moor ED, Speer JG, Matlock DK, et al. (2011) Effect of carbon and manganese on the quenching and partitioning response of CMnSi steels. ISIJ Inter 51: 137–144. doi: 10.2355/isijinternational.51.137
    [5] Nonaka T, Fujita N, Taniguchi Y, et al. (2007) Development of ultra-high-strength steel sheets with excellent formabilities. Materia Jpn 46: 108–110. doi: 10.2320/materia.46.108
    [6] Takahashi M (2002) High strength steel sheets for light weight auto-bodies. Bull Iron Steel Inst Jpn 7: 870–877.
    [7] Tomota Y, Tanimoto I, Kuroki K (1982) On the deformation behavior of ferrite-martensite: two-ductile-phase steels. T Jpn Soc Mech Eng A 48: 528–536. doi: 10.1299/kikaia.48.528
    [8] Sugimoto K, Sakaki T, Fukusato T, et al. (1985) Influence of martensite morphology on initial yielding and strain hardening in a 0.11–1.36Mn dual-phase steel. Tetsu-to-Hagane 71: 994–1001.
    [9] Kondo D, Kunishige K, Ueji R (2006) Effects of the grain size and volume fraction of second hard phase on mechanical properties of dual phase steel. Tetsu-to-Hagane 92: 457–463. doi: 10.2355/tetsutohagane1955.92.7_457
    [10] Jiang Z, Guan Z, Lian J (1995) Effects of microstructural variables on the deformation behaviour of dual-phase steel. Mater Sci Eng A-Struct 190: 55–64. doi: 10.1016/0921-5093(94)09594-M
    [11] Ogawa T, Dannoshita H, Maruoka K, et al. (2017) Microstructural evolution during cold rolling and subsequent annealing in low-carbon steel with different initial microstructures. J Mater Eng Perform 26: 3821–3830. doi: 10.1007/s11665-017-2849-6
    [12] Dannoshita H, Ogawa T, Maruoka K, et al. (2019) Effect of initial microstructures on austenite formation behavior during intercritical annealing in low-carbon steel. Mater Trans 60: 165–168. doi: 10.2320/matertrans.M2018298
    [13] Hall EO (1951) The deformation and ageing of mild steel: III discussion of results. Proc Phys Soc B 64: 747–753. doi: 10.1088/0370-1301/64/9/303
    [14] Petch NJ (1953) The orientation relationships between cementite and α-iron. J Iron Steel Inst 174: 25–28.
    [15] Takaki S, Kawasaki K, Kimura Y (2001) Mechanical properties of ultra fine grained steels. J Mater Process Tech 117: 359–363. doi: 10.1016/S0924-0136(01)00797-X
    [16] Furukimi O, Takeda Y, Yamamoto M, et al. (2017) Voids nucleation and growth examination during tensile deformation for IF steel by synchrotron X-ray laminography and EBSD. Tetsu-to-Hagane 103: 475–482. doi: 10.2355/tetsutohagane.TETSU-2017-011
    [17] Tohgo K, Ishii H, Hiramatsu K, et al. (1993) Influence of cementite volume fraction on mechanical properties and fracture toughness in spheroidized cementite steel: study on fracture behavior of particulate-reinforced composite. T Jpn Soc Mech Eng A 59: 1617–1624. doi: 10.1299/kikaia.59.1617
    [18] Fujita T, Kariya N, Nakamura N, et al. (2005) Effect of microstructure on elongation in cold-rolled high carbon steel sheets. Tetsu-to-Hagane 91: 616–622. doi: 10.2355/tetsutohagane1955.91.7_616
    [19] Maeda M, Shimamura J, Suzuki S (2017) Void formation by cementite and local misorientation evaluation during tensile deformation in high strength steel sheets. Tetsu-to-Hagane 103: 483–490. doi: 10.2355/tetsutohagane.TETSU-2016-106
    [20] Furukimi O, Niigaki S, Yamada N, et al. (2013) Local deformation energy and void formation behavior in 16%Cr ferritic steel. Tetsu-to-Hagane 99: 60–69. doi: 10.2355/tetsutohagane.99.60
  • Reader Comments
  • © 2019 the Author(s), licensee AIMS Press. This is an open access article distributed under the terms of the Creative Commons Attribution License (http://creativecommons.org/licenses/by/4.0)
通讯作者: 陈斌, bchen63@163.com
  • 1. 

    沈阳化工大学材料科学与工程学院 沈阳 110142

  1. 本站搜索
  2. 百度学术搜索
  3. 万方数据库搜索
  4. CNKI搜索

Metrics

Article views(4125) PDF downloads(680) Cited by(3)

Article outline

Figures and Tables

Figures(7)

/

DownLoad:  Full-Size Img  PowerPoint
Return
Return

Catalog