Research article Special Issues

Antibacterial activities of gel-derived Ag-TiO2-SiO2 nanomaterials under different light irradiation

  • Received: 23 December 2015 Accepted: 14 March 2016 Published: 17 March 2016
  • Gel-derived Ag-TiO2-SiO2 nanomaterials were prepared by sol-gel process to determine their disinfection efficiency under UV-C, UV-A, solar irradiations and in dark condition. The surface morphology and properties of gel-derived Ag-TiO2-SiO2 nanomaterials were characterized by X-ray diffraction (XRD), transmission electron microscopy (TEM) and BET specific surface area. The results showed that the average particle size of Ag-TiO2-SiO2 was around 10.9–16.3 nm. SiO2 mixed with TiO2 (the weight ratio of Si to Ti = 10:90) in the synthesis of Ag-TiO2-SiO2 by sol-gel process was found to increase the specific surface area of the obtained photocatalyst (164.5 m2g−1) as compared with that of commercial TiO2(P25) (53.1 m2g−1). Meanwhile, Ag doped in TiO2 (the mole ratio of Ag to TiO2 = 1%) decreased the specific surface area to 147.3 m2g−1. The antibacterial activities of gel-derived Ag-TiO2-SiO2 nanomaterials were evaluated by photocatalytic reaction against Escherichia coli bacteria (ATCC®25922). Ag-TiO2-SiO2 nanomaterials was observed to achieve higher disinfection efficiency than the catalyst without silver since both Ag nanoparticles and ions exhibit a strong antibacterial activity and promoted the e – h+ separation of TiO2. The bactericidal activity of Ag-TiO2-SiO2 nanomaterial under light irradiation was superior to that under dark and only light. The reaction time to achieve a reduction by 6 log of bacteria of UV-C light alone and Ag-TiO2-SiO2 with UV-C light irradiation were 30 and 5 minutes, respectively. In addition, the superior synergistic effect of Ag-TiO2-SiO2 under both UV-A and solar light as compared to that under UV-C counterpart could be ascribed to the red-shift of the absorbance spectrum of the Ag doped TiO2-based catalyst.

    Citation: Nhung Thi-Tuyet Hoang, Anh Thi-Kim Tran, Nguyen Van Suc, The-Vinh Nguyen. Antibacterial activities of gel-derived Ag-TiO2-SiO2 nanomaterials under different light irradiation[J]. AIMS Materials Science, 2016, 3(2): 339-348. doi: 10.3934/matersci.2016.2.339

    Related Papers:

  • Gel-derived Ag-TiO2-SiO2 nanomaterials were prepared by sol-gel process to determine their disinfection efficiency under UV-C, UV-A, solar irradiations and in dark condition. The surface morphology and properties of gel-derived Ag-TiO2-SiO2 nanomaterials were characterized by X-ray diffraction (XRD), transmission electron microscopy (TEM) and BET specific surface area. The results showed that the average particle size of Ag-TiO2-SiO2 was around 10.9–16.3 nm. SiO2 mixed with TiO2 (the weight ratio of Si to Ti = 10:90) in the synthesis of Ag-TiO2-SiO2 by sol-gel process was found to increase the specific surface area of the obtained photocatalyst (164.5 m2g−1) as compared with that of commercial TiO2(P25) (53.1 m2g−1). Meanwhile, Ag doped in TiO2 (the mole ratio of Ag to TiO2 = 1%) decreased the specific surface area to 147.3 m2g−1. The antibacterial activities of gel-derived Ag-TiO2-SiO2 nanomaterials were evaluated by photocatalytic reaction against Escherichia coli bacteria (ATCC®25922). Ag-TiO2-SiO2 nanomaterials was observed to achieve higher disinfection efficiency than the catalyst without silver since both Ag nanoparticles and ions exhibit a strong antibacterial activity and promoted the e – h+ separation of TiO2. The bactericidal activity of Ag-TiO2-SiO2 nanomaterial under light irradiation was superior to that under dark and only light. The reaction time to achieve a reduction by 6 log of bacteria of UV-C light alone and Ag-TiO2-SiO2 with UV-C light irradiation were 30 and 5 minutes, respectively. In addition, the superior synergistic effect of Ag-TiO2-SiO2 under both UV-A and solar light as compared to that under UV-C counterpart could be ascribed to the red-shift of the absorbance spectrum of the Ag doped TiO2-based catalyst.


    加载中
    [1] Hoffman MR, Martin ST, Choi W, et al. (1995) Environmental application of semiconductor photocatalysis. Chem Rev 95: 69–96. doi: 10.1021/cr00033a004
    [2] Robertson P (1996) Semiconductor photocatalysis: An environmentally acceptable alternative production technique and efluent treament process. J Cleaner Prod 4: 203–212.
    [3] Matsunga T, Tamada R, Wake H (1985) Photoelectrochemical sterilization of microbial-cells by semiconductor powders. FEMS Microbiol Lett 29: 211–214. doi: 10.1111/j.1574-6968.1985.tb00864.x
    [4] Rengaraj S, Li XZ (2006) Enhanced photocatalytic activity of TiO2 by doping with Ag for degradation of 2,4,6-trichlorophenol in Aqueous Suspension. J Mol Cataltsis A 243: 60–67. doi: 10.1016/j.molcata.2005.08.010
    [5] Katsumata H, Sada M, Nakaoka Y, et al. (2009) Photocatalytic degradation of diuron in aqueous solutions of platinized TiO2. J Hazard Mater 171: 1081–1087. doi: 10.1016/j.jhazmat.2009.06.110
    [6] Kalathil S, Khan MM, Banerjee AN, et al. (2012) A simple biogenic route to rapid synthesis of Au@TiO2 nanocomposites by electrochemically active biofilms. J Nanoparticle Res 14: 1051–1059. doi: 10.1007/s11051-012-1051-x
    [7] Fang J, Cao S-W, Wang Z, et al. (2012) Mesoporous plasmonic Au–TiO2 nanocomposites for efficient visible-light-driven photocatalytic water reduction. Int J Hydrogen Energy 37: 17853–17861.
    [8] Yu C, Cai D, Yang K, et al. (2010) Sol- gel derived S, I-codoped mesoporous TiO2 photocatalyst with high visible-light photocatalytic activity. J Phys Chem Solids 71: 1337–1343. doi: 10.1016/j.jpcs.2010.06.001
    [9] Yuranova T, Rincon AG, Bozzi A, et al. (2003) Antibacterial textiles prepared by RF-plasma and vacuum-UV mediated deposition of silver. J Photochem Photobiol 161: 27–34.
    [10] Grieken RV, Marugán J, Sordo C, et al. (2009) Photocatalytic inactivation of bacteria in water using suspended and immobilized silver-TiO2. Environmental 93: 112–118.
    [11] Sangchaya W, Sikonga L, Kooptarnond K (2012) Comparison of photocatalytic reaction of commercial P25 and synthetic TiO2-AgCl nanoparticles. Procedia Eng 32: 590–596. doi: 10.1016/j.proeng.2012.01.1313
    [12] Ubonchonlakate K, Sikong L, Tontai T, et al. (2011) P. aeruginosa Inactivation with silver and nickel doped TiO2 films coated on glass fibre roving. Adv Mater Res 150–151: 1726–1731.
    [13] Cho KH, Park JE, Osaka T, et al. (2005) The study of antimicrobial activity and preservative effects of nanosilver ingredient. Electrochim Acta 51: 956–960. doi: 10.1016/j.electacta.2005.04.071
    [14] Akhavan O, Ghaderi E (2009) Enhancement of antibacterial properties of Ag nanorods by electric field. Sci Technol Adv Mater 10: 015003.
    [15] Li M, Noriega-Trevino ME, Nino-Martinez N, et al. (2011) Synergistic Bactericidal Activity of Ag-TiO2 nanoparticles in Both Light and Dark Conditions. Environ Sci Technol 45: 8989–8995. doi: 10.1021/es201675m
    [16] Thiel J, Pakstis L, Buzby S, et al. (2007) Antibacterial properties of silver-doped. Small 3: 799–803. doi: 10.1002/smll.200600481
    [17] Scafani A, Palmisano L, Schiavello M (1990) Influence of the preparation methods of titanium dioxide on the photocatalytic degradation of phenol in aqueous dispersion. J Phys Chem 94: 829–832. doi: 10.1021/j100365a058
    [18] Viet-Cuong N, The-Vinh N (2009) Photocatalytic decomposition of phenol over N-TiO2-SiO2 catalyst under natural sunlight. J ExpNanosci 4: 233–242.
    [19] Hoang T-TN, Suc NV, Nguyen T-V (2015) Bactericidal activities and synergistic effects of Ag–TiO2 and Ag–TiO2–SiO2 nanomaterials under UV-C and dark conditions. Int J Nanotechnol 12: 367–379. doi: 10.1504/IJNT.2015.067894
    [20] Sun B, Sun S-Q, Li T, et al. (2007) Preparation and antibacterial activities of Ag-doped SiO2–TiO2 composite films by liquid phase deposition (LPD) method. J Mater Sci 42: 10085–10089. doi: 10.1007/s10853-007-2109-5
    [21] Chao HE, Yuan YU, Xingfanga HU (2003) Effect of silver doping on the phase transformation and grain growth of sol-gel titania powder. J Eur Ceramic Soci 23: 1457–1464. doi: 10.1016/S0955-2219(02)00356-4
    [22] Oliveri G, Ramis G, Busca G, et al. (1993) Thermal stability of vanadia-titania cataysts. J Mater Chem 3: 1239–1249. doi: 10.1039/JM9930301239
    [23] Shahverdi AR, Fakhimi A, Shahverdi HR, et al. (2007) Synthesis and effect of silver nanoparticles on the antibacterial activity of different antibiotics against Staphylococcus aureus and Escherichia coli. Nanomedicine 3: 168–171.
    [24] Smetana AB, Klabunde KJ, Marchin GR, et al. (2008) Biocidal activity of nanocrystalline silver powders and particles. Langmuir 24: 7457–7464. doi: 10.1021/la800091y
    [25] Yamanaka M, Hara K, Kudo J (2005) Bactericidal actions of a silver ion solution on Escherichia coli, studied by energy-filtering transmission electron microscopy and proteomic analysis. Appl Environ Microbiol 71: 7589–7593. doi: 10.1128/AEM.71.11.7589-7593.2005
    [26] Benabbou AK, Derriche Z, Felix C, et al. (2007) Photocatalytic inactivation of Escherischia coli. Effect of concentration of TiO2 and microorganism, nature, and intensity of UV irradiation. Appl Catal B Environ 76: 257–263.
    [27] Hassan Y, Ishtiaq AQ, Imran H, et al. (2013) Visible light photocatalytic water disinfection and its kinetics using Ag-doped titania nanoparticles. Environ Sci Pollut Res 21: 740–752.
    [28] Anpo M, Kishiguchi S, Ichihashi Y, et al. (2001) The design and development of second-generation titanium oxide photocatalysts able to operate under visible light irradiation by applying a metal ion-implantation method. Res Chem Intermediat 27: 459–467. doi: 10.1163/156856701104202101
    [29] Chen X, Lou Y, Samia ACS, et al. (2003) Coherency Strain Effects on the Optical Response of Core/Shell Heteronanostructures. Nano Lett 3: 799–803.
    [30] Park CH, Zhang SB, Wei SH (2002) Origin ofp-type doping difficulty in ZnO: The impurity perspective. Phys Rev 66: 073202. doi: 10.1103/PhysRevB.66.073202
    [31] Choi W, Termin A, Hoffmann M (1994) The Role of Metal Ion Dopants in Quantum-Sized TiO2: Correlation between Photoreactivity and Charge Carrier Recombination Dynamics. J Phys Chem 98: 13669–13679.
    [32] Mu W, Herrmann JM, Pichat P (1989) Room temperature photocatalytic oxidation of liquid cyclohexane into cyclohexanone over neat and modified TiO2. Catal Lett 3: 73–84. doi: 10.1007/BF00765057
    [33] Duonghong D, Borgarello E, Gratzel M (1981) Dynamics of light-induced water cleavage in colloidal systems. J Am Chem Soc 103: 4685–4690. doi: 10.1021/ja00406a004
  • Reader Comments
  • © 2016 the Author(s), licensee AIMS Press. This is an open access article distributed under the terms of the Creative Commons Attribution License (http://creativecommons.org/licenses/by/4.0)
通讯作者: 陈斌, bchen63@163.com
  • 1. 

    沈阳化工大学材料科学与工程学院 沈阳 110142

  1. 本站搜索
  2. 百度学术搜索
  3. 万方数据库搜索
  4. CNKI搜索

Metrics

Article views(4723) PDF downloads(1365) Cited by(1)

Article outline

Figures and Tables

Figures(4)

/

DownLoad:  Full-Size Img  PowerPoint
Return
Return

Catalog