Device performances and instabilities of the engineered active layer with different film thickness and composition ratios in amorphous InGaZnO thin film transistors

  • Received: 02 August 2020 Accepted: 08 September 2020 Published: 15 September 2020
  • The device performances and instabilities of the engineered active layer with different film thickness and composition ratios in amorphous InGaZnO thin film transistor prepared by RF-sputtering have been investigated. The engineered active layer devices were composed of an In and Zn rich front layer with thickness of 10 nm and a Ga rich back layer with thickness from 20 to 30 nm. The device instabilities were investigated under positive bias stress (PBS), negative bias illumination stress (NBIS) and high VGS and VDS stress. The device performances and the stability have been enhanced in channel engineered active layer a-IGZO TFTs due to the combination of the high conductive channel with In and Zn rich front layer and the passivation effects with the Ga rich back layer. The concurrent device degradation mechanism is suggested to explain the more severe device degradation under high VGS and VDS stress than the device degradation under PBS.

    Citation: Dong Geun Lee, Hwan Chul Yoo, Eun-Ki Hong, Won-Ju Cho, Jong Tae Park. Device performances and instabilities of the engineered active layer with different film thickness and composition ratios in amorphous InGaZnO thin film transistors[J]. AIMS Materials Science, 2020, 7(5): 596-607. doi: 10.3934/matersci.2020.5.596

    Related Papers:

  • The device performances and instabilities of the engineered active layer with different film thickness and composition ratios in amorphous InGaZnO thin film transistor prepared by RF-sputtering have been investigated. The engineered active layer devices were composed of an In and Zn rich front layer with thickness of 10 nm and a Ga rich back layer with thickness from 20 to 30 nm. The device instabilities were investigated under positive bias stress (PBS), negative bias illumination stress (NBIS) and high VGS and VDS stress. The device performances and the stability have been enhanced in channel engineered active layer a-IGZO TFTs due to the combination of the high conductive channel with In and Zn rich front layer and the passivation effects with the Ga rich back layer. The concurrent device degradation mechanism is suggested to explain the more severe device degradation under high VGS and VDS stress than the device degradation under PBS.


    加载中


    [1] Nomura K, Ohta H, Kamiya T, et al. (2003) Thin-film transistor fabrication in single-crystalline transparent oxide semiconductor. Science 300: 1269-1272. doi: 10.1126/science.1083212
    [2] Iwasaki T, Itagaki N, Den T, et al. (2007) Combinational approach to thin-film transistors using multicomponent semiconductor channels: An application to amorphous oxide semiconductors in In-Ga-Zn-O system. Appl Phys Lett 90: 242114. doi: 10.1063/1.2749177
    [3] Kim GH, Du Ahn B, Shin HS, et al. (2009) Effect of indium composition ratio on solution-processed nanocrystalline InGaZnO thin film transistors. Appl Phys Lett 94: 233501. doi: 10.1063/1.3151827
    [4] Jeon H, Na S, Moon M, et al. (2011) The effects of Zn ratio on the microstructure electrical properties of InGaZnO film. J Electrochem Soc 158: H949-H954. doi: 10.1149/1.3615534
    [5] Nomura K, Ohta H, Kamiya T, et al. (2004) Room-temperature fabrication of transparent flexible thin-film transistors using amorphous oxide semiconductors. Nature 432: 488-492. doi: 10.1038/nature03090
    [6] Yabuta H, Sano M, Abe K, et al. (2006) High-mobility thin-film transistor with amorphous InGaZnO4 channel fabricated by room temperature rf-magnetron sputtering. Appl Phys Lett 89: 112123. doi: 10.1063/1.2353811
    [7] Kim SM, Yu CG, Cho WJ, et al. (2017) Device characterization and design guideline of amorphous InGaZnO junctionless thin-film transistors. IEEE T Electron Dev 64: 2526-2532. doi: 10.1109/TED.2017.2696048
    [8] Lee SY, Kim DH, Chong E, et al. (2011) Effect of channel thickness on density of states in amorphous InGaZnO thin film transistor. Appl Phys Lett 98: 122105. doi: 10.1063/1.3570641
    [9] Kong D, Jung HK, Kim Y, et al. (2011) The effects of the active layer thickness on the negative bias stress-induced instability in amorphous InGaZnO thin-film transistors. IEEE Electr Device L 32: 1388-1390. doi: 10.1109/LED.2011.2161746
    [10] Cho EN, Kang JH, Yun I (2011) Effects of channel thickness variation on bias stress instability of InGaZnO thin-film transistors. Microelectron Reliab 51: 1792-1795. doi: 10.1016/j.microrel.2011.07.018
    [11] Wang D, Zhao W, Li H, et al. (2018) Drain current stress-induced instability in amorphous InGaZnO thin-film transistors with different active layer thickness. Materials 11: 559. doi: 10.3390/ma11040559
    [12] Kim KM, Jeon WH, Kim DI, et al. (2011) Low-temperature solution processing of AlInZnO/InZnO dual-channel thin-film transistor. IEEE Electr Device L 32: 1242. doi: 10.1109/LED.2011.2160612
    [13] Jeong WH, Kim KM, Kim DI, et al. (2012) The effects of dual-active-layer modulation on a low-temperature solution-processed oxide thin-film transistor. IEEE T Electron Dev 59: 2149-2152. doi: 10.1109/TED.2012.2198064
    [14] Hong SH, Park JW, Kim HJ, et al. (2016) A review of multi-stacked active-layer structures for solution-processed semiconductor thin-film transistors. JID 17: 93-101.
    [15] Liu PT, Chou YT, Teng LF, et al. (2011) Ambient stability enhancement of thin-film transistor with InGaZnO capped with InGaZnO:N bilayer stack channel layers. IEEE Electr Device L 32: 1397-1399. doi: 10.1109/LED.2011.2163181
    [16] Lee JH, Park YH, Shin JW, et al. (2019) Device performances and instabilities of channel engineered amorphous InGaZnO thin film transistors. Microelectron Reliab 100-101: 113397-13402. doi: 10.1016/j.microrel.2019.113397
    [17] Kim DH, Jeong HK, Lee SY (2011) Effect of interface states on the instability under temperature stress in amorphous SiInZnO thin film transistor. Appl Phys Lett 99: 162101. doi: 10.1063/1.3645597
    [18] Li Y, Pei YL, Hu RQ, et al. (2014) Effect of channel thickness on electrical performance of amorphous IGZO thin-film transistor with atomic layer deposited alumina oxide dielectric. Curr Appl Phys 14: 941-945. doi: 10.1016/j.cap.2014.04.011
    [19] Cho MH, Kim MJ, Seul H, et al. (2019) Impact of cation compositions on the performance of thin-film transistors with amorphous indium gallium zinc oxide grown through atomic layer deposition. JID 20: 73-80.
    [20] Huang CY, Huang CP, Chen H, et al. (2020) A self-powered ultraviolet photodiode using an amorphous InGaZnO/p-silicon nanowire heterojunction. Vacuum 180: 109619. doi: 10.1016/j.vacuum.2020.109619
    [21] Kim SJ, Lee SY, Lee YW, et al. (2011) Effect of channel layer thickness on characteristics and stability of amorphous hafnium-indium-zinc oxide thin film transistors. Jpn J Appl Phys 50: 024104. doi: 10.1143/JJAP.50.024104
    [22] Park HP, Kim SW, Shin JW, et al. (2018) Effects of the compositional ratios of sputtering target on the device performance and instability in amorphous InGaZnO thin film transistors. Microelectron Reliab 88-90: 873-878. doi: 10.1016/j.microrel.2018.06.052
    [23] Huang CY (2020) The effect of Gamma irradiation on the stability of amorphous InGaZnO metal-semiconductor-metal UV photodetectors. J Non-cryst Solids 546: 120292. doi: 10.1016/j.jnoncrysol.2020.120292
    [24] Kim JH, Park EK, Kim MS, et al. (2018) Bias and illumination instability analysis of solution-processed a-InGaZnO thin-film transistors with different composition ratios. Thin Solid Films 645: 154-159. doi: 10.1016/j.tsf.2017.09.054
    [25] Lee SM, Yu CG, Cho WJ, et al. (2012) Hot carrier degradation of InGaZnO thin film transistors under light illumination at the elevated temperature. Solid State Electron 72: 88-92. doi: 10.1016/j.sse.2012.02.010
    [26] Urakawa S, Tomai S, Ueoka Y, et al. (2013) Thermal analysis of amorphous oxide thin-film transistor degraded by combination of joule heating and hot carrier effect. Appl Phys Lett 102: 053506. doi: 10.1063/1.4790619
    [27] Im H, Song H, Jeong J, et al. (2015) Effects of defect creation on bidirectional behaviour with hump characteristics of InGaZnO TFTs under bias and thermal stress. Jpn J Appl Phys 54: 03CB03.
    [28] Choi S, Kim H, Jo C, et al. (2015) The effect of gate and drain fields on the completion between donor-like state creation and local electron trapping in In-Ga-Zn-O thin-film transistors under current stress. IEEE Electr Device L 36: 1336-1339. doi: 10.1109/LED.2015.2487370
  • Reader Comments
  • © 2020 the Author(s), licensee AIMS Press. This is an open access article distributed under the terms of the Creative Commons Attribution License (http://creativecommons.org/licenses/by/4.0)
通讯作者: 陈斌, bchen63@163.com
  • 1. 

    沈阳化工大学材料科学与工程学院 沈阳 110142

  1. 本站搜索
  2. 百度学术搜索
  3. 万方数据库搜索
  4. CNKI搜索

Metrics

Article views(3052) PDF downloads(138) Cited by(0)

Article outline

Figures and Tables

Figures(10)  /  Tables(2)

/

DownLoad:  Full-Size Img  PowerPoint
Return
Return

Catalog