Basalt, glass and carbon fibers and their fiber reinforced polymer composites under thermal and mechanical load

  • Received: 08 September 2016 Accepted: 02 November 2016 Published: 15 November 2016
  • In order to enhance customer acceptance cost optimization is essential regarding future drive trains, like the fuel cell drive. Regarding the pressure vessels, which are needed to store the hydrogen, carbon fibers are the main cost driver. Therefore basalt fibers were identified as a cost effective alternative in previous studies. As fire load is one of the crucial tests in pressure vessel examination, the authors focused on the effect of thermal load on the mechanical properties of basalt fibers and their composites in this work. Therefor tensile tests were performed on impregnated basalt rovings and competing E-glass and carbon rovings after exposition to high temperatures between 100 and 600 °C. Furthermore residual tensile strength of unidirectional basalt-, E-glass-, and carbon reinforced polymers was tested after one-sided thermal load. Both experiments showed that basalt had higher tensile strength at low temperatures or shorter exposition times compared to glass. Yet degradation was more severe and strength was lower at higher temperatures or longer exposition times.

    Citation: Eduard Kessler, Rainer Gadow, Jona Straub. Basalt, glass and carbon fibers and their fiber reinforced polymer composites under thermal and mechanical load[J]. AIMS Materials Science, 2016, 3(4): 1561-1576. doi: 10.3934/matersci.2016.4.1561

    Related Papers:

  • In order to enhance customer acceptance cost optimization is essential regarding future drive trains, like the fuel cell drive. Regarding the pressure vessels, which are needed to store the hydrogen, carbon fibers are the main cost driver. Therefore basalt fibers were identified as a cost effective alternative in previous studies. As fire load is one of the crucial tests in pressure vessel examination, the authors focused on the effect of thermal load on the mechanical properties of basalt fibers and their composites in this work. Therefor tensile tests were performed on impregnated basalt rovings and competing E-glass and carbon rovings after exposition to high temperatures between 100 and 600 °C. Furthermore residual tensile strength of unidirectional basalt-, E-glass-, and carbon reinforced polymers was tested after one-sided thermal load. Both experiments showed that basalt had higher tensile strength at low temperatures or shorter exposition times compared to glass. Yet degradation was more severe and strength was lower at higher temperatures or longer exposition times.


    加载中
    [1] Regulation (EC) no. 443/2009 of the European Parliament and of the Council. Off J Eur Union.
    [2] Mori D, Hirose K (2009) Recent challenges of hydrogen storage technologies for fuel cell vehicles. Int J Hydrogen Energy 34: 4569–4574.
    [3] Hua TQ, Ahluwalia RK, Peng JK, et al. (2011) Technical assessment of compressed hydrogen storage tank systems for automotive applications. Int J Hydrogen Energy 36: 3037–3049.
    [4] Kessler E, Gadow R, Weichand P (2015) Investigation of mechanical properties of filament wound unidirectional basalt fiber reinforced polymers for automotive and pressure vessel application. ICCM 20, 20th International Conference on Composite Materials, Copenhagen, Denmark.
    [5] Gambone LR, Wong JY (2007) Fire protection strategy for compressed hydrogen-powered vehicles. 2nd International Conference on Hydrogen Safety, San Sebastian, Spain.
    [6] Ruban S, Heudier L, Jamois D, et al. (2012) Fire risk on high-pressure full composite cylinders for automotive applications. Int J Hydrogen Energy 37: 17630–17638.
    [7] Artemenko SE (2003) Polymer composite materials made from carbon, basalt and glass fibres. Structure and properties. Fibre Chem 35: 226–229.
    [8] Subramanian RV, Austin HF (1980) Silane coupling agents in basalt-reinforced polyester composites. Int J Adhes Adhes 1: 50–54.
    [9] Deak T, Czigany T (2009) Chemical composition and mechanical properties of basalt and glass fibers: a comparison. Text Res J 79: 645–651.
    [10] Gadow R, Weichand P (2014) Novel intermediate temperature ceramic composites, materials and processing for siloxane based basalt fiber composites. Key Eng Mater 611: 382–390.
    [11] Yin Y, Binner JGP, Cross TE, et al. (1994) The oxidation behaviour of carbon fibres. J Mater Sci 29: 2250–2254.
    [12] Feih S, Mouritz AP, Mathys Z, et al. (2007) Tensile strength modeling of glass fiber-polymer composites in fire. J Compos Mater 41: 2387–2410.
    [13] Feih S, Manatpon K, Mathys Z, et al. (2009) Strength degradation of glass fibers at high temperatures. J Mater Sci 44: 392–400.
    [14] Feih S, Boiocchi E, Kandare E, et al. (2009) Strength degradation of glass and carbon fibres at high temperature. ICCM 17, 17th International Conference on Composite Materials, Edinburgh, Scotland.
    [15] Jenkins PG, Riopedre-Méndez S, Sáez-Rodríguez E, et al. (2015) Investigation of the strength of thermally conditioned basalt and E-glass fibres. ICCM 20, 20th International Conference on Composite Materials, Copenhagen, Denmark.
    [16] Bhat T, Chevali V, Liu X, et al. (2015) Fire structural resistance of basalt fibre composite. Compos Part A-Appl S 71: 107–115.
    [17] Morozov NN, Bakunov VS, Morozov EN, et al. (2001) Materials based on basalts from the European north of Russia. Glass Ceram 58: 100–104.
    [18] Sim J, Park C, Moon DY (2005) Characteristics of basalt fiber as a strengthening material for concrete structures. Compos Part B-Eng 36: 504–512.
    [19] German Institute for Standardization DIN 65 382 (1988) Aerospace; Reinforcement fibers for plastics; Tensile test of impregnated yarn test specimens.
    [20] International Organization for Standardization ISO 527-5 (2010) Plastics—Determination of tensile properties. Part 5: Test conditions for unidirectional fibre-reinforced plastic composites.
    [21] Feih S, Mouritz AP (2012) Tensile properties of carbon fibres and carbon fibre-polymer composites in fire. Compos Part A-Appl S 43: 765–772.
    [22] Incotelogy GmbH (2015) Basalt rovings technical data sheet.
    [23] Makhova MF (1968) Crystallization of basalt fibers. Glass Ceram 25: 672–674.
    [24] Kessler E, Gadow R, Semmler C (2016) Apparent hoop tensile strength of basalt fiber and hybrid fiber reinforced polymers. Proceedings SAMPE Technical Conference, Long Beach, USA.
  • Reader Comments
  • © 2016 the Author(s), licensee AIMS Press. This is an open access article distributed under the terms of the Creative Commons Attribution License (http://creativecommons.org/licenses/by/4.0)
通讯作者: 陈斌, bchen63@163.com
  • 1. 

    沈阳化工大学材料科学与工程学院 沈阳 110142

  1. 本站搜索
  2. 百度学术搜索
  3. 万方数据库搜索
  4. CNKI搜索

Metrics

Article views(6913) PDF downloads(1744) Cited by(39)

Article outline

Figures and Tables

Figures(13)  /  Tables(3)

Other Articles By Authors

/

DownLoad:  Full-Size Img  PowerPoint
Return
Return

Catalog