Magnetic properties of Sm5Fe17 melt-spun ribbons and their borides

  • Received: 24 August 2015 Accepted: 20 October 2015 Published: 22 October 2015
  • Sm5Fe17 melt-spun ribbons exhibited low coercivity and partly or mostly consisted of the amorphous phase. Annealing of Sm5Fe17 melt-spun ribbon resulted in the formation of the Sm5Fe17 phase. The annealed Sm5Fe17 melt-spun ribbon exhibited a high coercivity. It was found that the addition of B to the Sm5Fe17 alloy resulted in the promotion of the Sm2Fe14B phase. Annealed Sm5Fe17Bx (x = 0.5) melt-spun ribbons consisted of the Sm5Fe17 phase together with the Sm2Fe14B and SmFe2 phases. On the other hand, annealed Sm5Fe17Bx (x = 1.0-1.5) melt-spun ribbons consisted of the Sm2Fe14B and SmFe2 phases without the Sm5Fe17 phase. The resultant Sm5Fe17Bx (x = 1.0-1.5) melt-spun ribbons still showed a coercivity of around 2 kOe. The annealed Sm5Fe17 melt-spun ribbon exhibited a high coercivity over 25 kOe and a remanence of 40 emu/g, whereas the annealed Sm5Fe17B1.0 melt-spun ribbon exhibited a high remanence of 65 emu/g and a coercivity of 2.0 kOe.

    Citation: Tetsuji Saito, Daisuke Nishio-Hamane. Magnetic properties of Sm5Fe17 melt-spun ribbons and their borides[J]. AIMS Materials Science, 2015, 2(4): 392-400. doi: 10.3934/matersci.2015.4.392

    Related Papers:

  • Sm5Fe17 melt-spun ribbons exhibited low coercivity and partly or mostly consisted of the amorphous phase. Annealing of Sm5Fe17 melt-spun ribbon resulted in the formation of the Sm5Fe17 phase. The annealed Sm5Fe17 melt-spun ribbon exhibited a high coercivity. It was found that the addition of B to the Sm5Fe17 alloy resulted in the promotion of the Sm2Fe14B phase. Annealed Sm5Fe17Bx (x = 0.5) melt-spun ribbons consisted of the Sm5Fe17 phase together with the Sm2Fe14B and SmFe2 phases. On the other hand, annealed Sm5Fe17Bx (x = 1.0-1.5) melt-spun ribbons consisted of the Sm2Fe14B and SmFe2 phases without the Sm5Fe17 phase. The resultant Sm5Fe17Bx (x = 1.0-1.5) melt-spun ribbons still showed a coercivity of around 2 kOe. The annealed Sm5Fe17 melt-spun ribbon exhibited a high coercivity over 25 kOe and a remanence of 40 emu/g, whereas the annealed Sm5Fe17B1.0 melt-spun ribbon exhibited a high remanence of 65 emu/g and a coercivity of 2.0 kOe.


    加载中
    [1] Kamprath H, Liu NC, Hedge H, et al. (1990) Magnetic properties of Sm-Fe-Ti-Al sputtered films with i H c greater than 30 kOe. J Appl Phys 67: 4948-4950. doi: 10.1063/1.344743
    [2] Stadelmaier HH, Schneider G, Henig ETh, et al. (1991) Magnetic Fe17R5 in the Fe-Nd and Fe(-Ti)-Sm systems, and other phases in Fe-Nd. Mater Lett 10: 303-309. doi: 10.1016/0167-577X(91)90142-S
    [3] Katter M, Wecker J, Schultz L, et al. (1990) Preparation of highly coercive Sm-Fe-Ti by rapid quenching. Appl Phys Lett 56: 1377-1379. doi: 10.1063/1.102518
    [4] Cadieu FJ, Hegde H, Rani R, et al. (1991) Cell volume expansion in Sm5(Fe, T)17, T = Ti, V, magnetic phases. Mater Lett 11: 284-285. doi: 10.1016/0167-577X(91)90203-I
    [5] Saito T, Ichihara M (2007) Synthesis and magnetic properties of Sm5Fe17 hard magnetic phase. Scripta Mater 57:457-460. doi: 10.1016/j.scriptamat.2007.05.037
    [6] Saito T (2007) Synthesis and magnetic properties of (Nd1-xSmx)5Fe17 (x = 0-1) phase. Appl Phys Lett 91: 072503-1-072503-3. doi: 10.1063/1.2770771
    [7] Saito T (2007) High coercivity in Sm5Fe17 melt-spun ribbon. J Alloys Compd 440: 315-318. doi: 10.1016/j.jallcom.2006.09.011
    [8] Saito T, Miyoshi H, Hamane DN (2012) Structures and magnetic properties of Sm5Fe17 melt-spun ribbon. J Appl Phys 111: -.
    [9] Kim DH, Zhang Y, Hadjipanayis GC (1998) Magnetic properties of Sm-Co-B-based nanocomposite magnets. J Magn Magn Mater 190: 302-306. doi: 10.1016/S0304-8853(98)00322-9
    [10] You C, Zhang ZD, Sun XK, et al. (2001) Phase transformation and magnetic properties of SmCo7-xBx alloys prepared by mechanical alloying. J Magn Magn Mater 234: 395-400. doi: 10.1016/S0304-8853(01)00435-8
    [11] Gapalan R, Xiong XY, Ohkubo T, et al. (2005) Nanoscale microstructure and magnetic properties of melt-spun Sm(Co0.725Fe0.1Cu0.12Zr0.04B0.015)7.4 ribbons. J Magn Magn Mater 295: 7-20. doi: 10.1016/j.jmmm.2004.12.033
    [12] Herbst JF (1991) R2Fe14B materials: Intrinsic properties and technological aspects. Rev Mod Phys 63: 819-898. doi: 10.1103/RevModPhys.63.819
    [13] Buschow KHJ (1971) The samarium-iron system. J Less-Common Metals 25: 131-134. doi: 10.1016/0022-5088(71)90124-X
    [14] Kim HT, Xiao QF, Zhang ZD, et al. (1997) Phases of melt-spun Sm1-xFe7+x alloys and magnetic properties of their nitrides. J Magn Magn Mater 173: 295-301. doi: 10.1016/S0304-8853(97)00169-8
  • Reader Comments
  • © 2015 the Author(s), licensee AIMS Press. This is an open access article distributed under the terms of the Creative Commons Attribution License (http://creativecommons.org/licenses/by/4.0)
通讯作者: 陈斌, bchen63@163.com
  • 1. 

    沈阳化工大学材料科学与工程学院 沈阳 110142

  1. 本站搜索
  2. 百度学术搜索
  3. 万方数据库搜索
  4. CNKI搜索

Metrics

Article views(4561) PDF downloads(1125) Cited by(2)

Article outline

Figures and Tables

Figures(9)

Other Articles By Authors

/

DownLoad:  Full-Size Img  PowerPoint
Return
Return

Catalog